摘要： The effect of Cu content on the evolution of defects in Fe-x%Cu alloys (x= 0.15, 0.3, and 0.6) were investigated using Positron Annihilation Lifetime Spectroscopy. The vacancy-type and Cu-vacancy complexes defects were respectively produced by quenching from 1173 K and cold-rolled deformation followed by isochronal annealing. The isochronal annealing results obtained by PALS showed that Cu-vacancy complexes delayed the complete recovery of vacancy-type defects and the complete recovery temperature increased with the content of Cu in 30% deformed Fe-Cu alloys. The increment of Cu content also restrained the migration of vacancies in as-quenched Fe-Cu alloys.
分类： 物理学 >> 凝聚态:结构、力学和热性能 提交时间： 2017-03-26
摘要： Cu precipitates played a key factor in irradiation induced hardening and embrittlement of reactor pressure vessel (RPV).In this work, two kinds of Fe-Cu model alloys with different Cu contents irradiated by Fe ion at 573 K were investigated using positron annihilation techniques and SEM. Doppler Broadening Spectroscopy(DBS) results indicated that with the irradiation dose increased from 0.1 dpa to 1.2 dpa, more vacancy-type defects were induced during Fe ion irradiation, and with different Cu contents, defects condition had few changes. Coincident Doppler Broadening (CDB) results indicated Cu precipitates were formed during the irradiation, which could be verified through the SEM results. The CDB results also showed that the Cu precipitates were the same at 0.1 dpa between the samples with different Cu contents. In Fe0.6Cu samples, more Cu precipitates were formed than that of Fe0.3Cu sample at 1.2 dpa.
点击量
待评议
点击量
下载量
评论